Wed Nov 19 16:11:00 2003

No Chuck it would not! Super Quench is not magic just a fast quench.  To do
the job the steel has to have the carbon content.  Hey you know that.  Might
work with 1045, but 1060 would be better.  1080 would be great.  4140 or
other alloy steels could also do the job, but not mild steel, even the evil
A 36.

Dave Smucker
----- Original Message ----- 
From: "Chuck Robinson" <[email protected]>
To: <[email protected]>
Sent: Wednesday, November 19, 2003 2:20 PM
Subject: Re: [TheForge] Suggestions needed for scroungeable steel

> You can heat treat mild steel in Gunthers super quench, and it should be
> hard enough for your application.
> Chuck
> ----- Original Message -----
> From: "Bruce Freeman" <[email protected]>
> To: <[email protected]>
> Sent: Wednesday, November 19, 2003 7:43 AM
> Subject: Re: [TheForge] Suggestions needed for scroungeable steel
>
>
> > Pete,
> > This particular TH will be quite simple.  The ram face IS the hammer
> > face.  No upper tooling.  Hence it needs to be hard enough not to
> > mushroom when it strikes a tool.  I expect to harden and temper it like
> > an ordinary hammer face.
> > Bruce
> > NJ
> >
> > >>> [email protected] 11/18/2003 11:33:20 PM >>>
> >
> > Bruce:
> > I'd respectfully argue that a hard face on a treadle hammer is not
> > desirable. A softer face will "stick" to a struck tool allowing greater
> >
> > latitude in alignment. With a hard face, more struck tools go flying to
> >
> > mysterious locations where they hide for years.    Pete F
> >
> > Bruce Freeman wrote:
> >
> > >I'm designing another treadle hammer, a lightweight job.  I want the
> > ram
> > >to be 20#.  What would be ideal is square or roundstock of about 2
> > >sq.in. in cross-section (i.e., 2" square or 2.25" round) and about
> > 18"
> > >long.
> > >
> > >Ideally, the material would be suitable for use as a hammer, with
> > >ordinary hardening & tempering.  Exotic materials not needed, but
> > mild
> > >steel wouldn't be appropriate unless faced with tool steel (a
> > >possibility I'd prefer to avoid).
> > >
> > >Since I prefer to design in scroungeable materials, I could use some
> > >suggestions as to sources of such steel.  The truck axles I've seen
> > are
> > >of smaller diameter than this (though I've seen tractors with axles
> > of
> > >3" dia.).  Track pins seem to be shorter than this - like 8" or so.
> > >Anyone have any other suggestions - preferably of materials you'd
> > have
> > >no particular trouble scrounging yourself?
> > >
> > >Thanks in advance,
> > >
> > >Bruce
> > >NJ
> > >
> > >
> > >
> > >
> > >
> > >
> > >
> > >--- StripMime Report -- processed MIME parts ---
> > >multipart/alternative
> > >  text/plain (text body -- kept)
> > >  text/html
> > >The reason this message is shown is because the post was in HTML
> > >or had an attachment.  Attachments are not allowed.  To learn how
> > >to post in Plain-Text go to: http://www.expita.com/nomime.html  ---
> > >_______________________________________________
> > >http://mailman.qth.net/mailman/listinfo/theforge
> > >theforge mail list group photo site is
> > >http://www.photoaccess.com
> > >Login:  [email protected]
> > >password:  anvil
> > >___________
> > >
> > >
> > >
> > >
> > >
> >
> > _______________________________________________
> > http://mailman.qth.net/mailman/listinfo/theforge
> > theforge mail list group photo site is
> > http://www.photoaccess.com
> > Login:  [email protected]
> > password:  anvil
> > ___________
> >
> >
> >
> >
> >
> > --- StripMime Report -- processed MIME parts ---
> > multipart/alternative
> >   text/plain (text body -- kept)
> >   text/html
> > The reason this message is shown is because the post was in HTML
> > or had an attachment.  Attachments are not allowed.  To learn how
> > to post in Plain-Text go to: http://www.expita.com/nomime.html  ---
> > _______________________________________________
> > http://mailman.qth.net/mailman/listinfo/theforge
> > theforge mail list group photo site is
> > http://www.photoaccess.com
> > Login:  [email protected]
> > password:  anvil
> > ___________
> >
> >
>
>
> _______________________________________________
> http://mailman.qth.net/mailman/listinfo/theforge
> theforge mail list group photo site is
> http://www.photoaccess.com
> Login:  [email protected]
> password:  anvil
> ___________
>
>
>