[Dan Tull]

Kevin,
That's why it's in all caps.
Directions say "preheating not recommended".

Run full width beads. Did you remember I said no call backs? That means no
"delaminating
from the body" also.

Note: you say "hard faceing rod", That's what also is cool, is that you are
not grinding
(sanding) on hard stuff. Less rock consumption.  Then you use a flatter to
work harden.

The added benefit of joining tool to mild is great for making hardie
tools,etc.

dan tull
georgia
abba, afc, S.C. psba, obg,sofa
----- Original Message ----- 
From: "Kevin Donahoe" <flyinpig@go-concepts.com>
To: <theforge@mailman.qth.net>
Sent: Sunday, July 20, 2003 3:59 PM
Subject: RE: [TheForge] Anvil Refacing


> Dan,
>
> No preheat on the anvil?  do you run short/spaced welds to prevent the
steel
> face from delaminating from the body?
>
> Also handy is to form carbon arc rods to fill the pritchel/hardy holes so
> there's minimum of grinding out small inside edges of over run hard facing
> rod.
>
> Kevin Donahoe
> Flying Pig Forge
> Morrow, OH